Electronics Forum | Wed Apr 13 21:47:32 EDT 2005 | Dhanish
In production,we are seeing high defect for Hair Line Solder Shorts for PTH connector and the Hair Line is too tiny that X-Ray and ICT could not detect.Any suggestion on how we can resolve or at least detect this upfront.
Electronics Forum | Sat Jul 11 03:01:29 EDT 2020 | researchmfg
The bubble inside BGA ball locate at via in pad and apply the resin plug hole.You shall check the cooper plating quality on PCB pad. If there is thin plating or broken on the pad then air will come from the resin plugged via and be trapped inside the
Electronics Forum | Tue Jul 18 00:02:41 EDT 2023 | hazira1991
Yes. i do check all the parameter all seams good. I did compare my solder paste printing and profile with previous lot that did not have any BGA solder short issue which we run at the same line did not have any much difference. During rework also i
Electronics Forum | Tue Apr 24 16:06:33 EDT 2007 | coop
I was just wondering if anybody has noticed a greenish/muddy color to their solder. It is just a very thin layer that can be easily be skimmed away but comes back shortly, I was just wondering if this an indication of a contaminated solder pot, we ha
Electronics Forum | Mon May 18 22:54:04 EDT 1998 | Dave F
.025" pitch so the only problem we run into is too much HASL on the adhesive side causing improper glue dispense. | | As Earl keeps saying HASL thickness is hard to impossible to control. I think we need to look hard at OSP's again but then you get
Electronics Forum | Thu Apr 14 18:51:19 EDT 2005 | KEN
What side is the short occuring on. Topside or bottom (solder) side? 2. Pitch of hole pattern = ? 3. Your x-ray may not have the resolution or DSP capable of detecting this defect. How does your profile look? Is this a true short or the result
Electronics Forum | Thu Feb 22 09:56:21 EST 2001 | blnorman
An adhesive, is an adhesive, is an adhesive. Yes most will thin when exposed to elevated temperature, but that's only for a short time. As cross-linking starts, viscosity increases. Having made countless numbers of adhesively bonded samples in the
Electronics Forum | Fri May 03 16:06:44 EDT 2013 | hegemon
To be short, no change in profile is going to get you through this. As I recall the point of hard gold is to retard the wetting process, so no surprise here. For example a connector might have hard gold plating at the mating surface, but not at t
Electronics Forum | Thu Apr 14 11:03:51 EDT 2005 | patrickbruneel
All possible causes aside, how can a dead short pass your ICT unless the connector is not probed.
Electronics Forum | Thu Apr 14 09:21:52 EDT 2005 | pr
What kind of wave are you using? Is this an old job and a new problem? Sounds like dross shorting to me, Make sure the wave is flowing over the back plate (at least when the board hits it). good luck, pr