Electronics Forum | Wed Jan 14 08:28:15 EST 1998 | Allison
Contact your solder paste manufacturer and get the reflow profile recommended for that particular paste. Then, duplicate that reflow profile on your oven. You will need to use thermocouples. You may have to tweak this profile a little. | We use no
Electronics Forum | Tue Jul 13 19:00:29 EDT 1999 | JohnW
| Hi All, | Does any one experienced the solder on gold finger after | reflow. Its about 5 to 8 mils diameter . | We'd clean the entire screen printer, mounter & reflow as well, | but doesn't help much. | | Mr Kong..... Solder on gold is a age old
Electronics Forum | Wed Jul 14 10:58:25 EDT 1999 | Upinder Singh
| | Hi All, | | Does any one experienced the solder on gold finger after | | reflow. Its about 5 to 8 mils diameter . | | We'd clean the entire screen printer, mounter & reflow as well, | | but doesn't help much. | | | | | Mr Kong..... | | Solder
Electronics Forum | Mon Jul 19 16:56:22 EDT 2004 | exmaintenanceleader
okay, add more flux first and try, pcb surface is not copper already, if more flux helps, than your pcb surface should be ok if not than mehanically cleaning the surface please, (like your car at home 'pol�roz�s-hungaian' I do not know the engli
Electronics Forum | Thu Nov 03 02:34:46 EST 2005 | Rosewood
We've recently encountered some problems with wire bond strengths. I'm looking for anybody that has had some experience with different types of substrate contamination and methods for cleaning. There is no visible contamination on the gold pads, bu
Electronics Forum | Sun May 16 03:38:49 EDT 1999 | Zambri
I'm running memory module product- SMT double reflow ( 12 modules per panel). I'm using the epoxy base solder paste in order to reduce the flux spattering problem onto the gold finger which could lead to the intermittent contact problem. I don't fa
Electronics Forum | Mon Jan 19 20:01:11 EST 1998 | Steve Gregory
| We use no clean paste and sometimes experience | flux splattering which gives spot on gold fingers. | Need help in analize the cause. thx. Dominic, That is STILL a problem huh? It's a tough one to solve sometimes...especially when you have as
Electronics Forum | Fri Jul 02 09:54:02 EDT 1999 | John Thorup
| | | | We are wave soldering some fabs with a lot of unmasked trace area along the edges. The trace area is solid copper covered with tin / lead, no masking, no components along the edges, same on solder side and component side (goofy board design)
Electronics Forum | Fri Jul 02 10:06:17 EDT 1999 | John Thorup
| | | | We are wave soldering some fabs with a lot of unmasked trace area along the edges. The trace area is solid copper covered with tin / lead, no masking, no components along the edges, same on solder side and component side (goofy board design)
Electronics Forum | Sat Apr 04 15:38:10 EST 1998 | Sam Forman, MicroCoat Technologies
| I will be starting a conformal coating process soon, I am looking for any pointers on | 1) Best method for masking components, tape mask, liqued mask | 2) Which is best Spray or Dip? | 3) Compatiblity with no clean solder paste (flux residue) |