Electronics Forum | Tue Dec 02 14:31:48 EST 2008 | dontfeedphils
Hey guys, just joined the site and I'm looking for some help. In our coating department we are running a Asymtek C-740 with a Jet and film coater. The coating that we are using is Humiseal 1B73 acrylic. The problem that we are having is that the C
Electronics Forum | Sat Dec 13 17:46:27 EST 2008 | ysutariya
If you're military then you're probably just needing standard 130Tg FR4 and tin-lead finish. I would check two things: 1. Bake temperature: Isola recommends 300F for 4 hours to drive moisture out. Lower baking temperatures do not require a linea
Electronics Forum | Wed Jan 14 18:23:05 EST 2009 | boardhouse
konrad, Here are a couple of things that can affect color. 1) Material color is the major, 2) Matte green from Enthone would be different in shad than Matte green from Taiyo. 3) Solder mask is two parts, One the green mask, two the hardner, having t
Electronics Forum | Wed Jan 21 10:27:27 EST 2009 | gidster
Ok. As you know the machines changed a bit after > 95 due to CE regulations. > > There are no drawing > on board/box level in Panasert > machines. > > However normaly i`ts the 100 volts > thats "shorting out" the machine and shuts it > down. C
Electronics Forum | Sun Jan 25 17:40:16 EST 2009 | cuperpeter
Hello All, I have a problem with nonwetting Au finish after second cycle of reflow soldering doublesided boards. Solder nonwetted pcb pads (is wicked to component terminations) Either these pads or some of non component pads became discoloured from
Electronics Forum | Tue Feb 03 16:42:50 EST 2009 | cuperpeter
Hello All, > > I have a problem with nonwetting Au > finish after second cycle of reflow soldering > doublesided boards. Solder nonwetted pcb pads (is > wicked to component terminations) Either these > pads or some of non component pads became
Electronics Forum | Tue Feb 03 14:19:29 EST 2009 | grics
I would agree if you have a board to setup the process. But sometimes this doesn't work... If for some reason if the customers AVL has a Lead Free BGA and I am running Leaded paste (yes this really happens!), you will need to run hotter to get your
Electronics Forum | Wed Feb 04 03:20:05 EST 2009 | smartasp
Hi All Reflow Gurus I have learnt that my process engineers do not consider the heat resistance, of the components when creating a reflow profile but rather try to stick to the paste recommendation. This has lead to a field recall as one component h
Electronics Forum | Wed Mar 18 16:50:20 EDT 2009 | khowell
There are many users of SN100C in reflow. SN100C was originally introduced as a wave solder alloy which offered cost savings over SAC, no solder pot erosion, and high fluidity. Since it is eutectic, no plastic range, the joints have a smooth, shiny
Electronics Forum | Fri Mar 27 10:04:51 EDT 2009 | ericthered
We have been having problems with proper wetting when running mainly lead free but also leaded solder in our Ersa Hotflow 3. Solder either often looks grainy or doesn't flow over the whole pad. This is generally the case when my profile is 170 firs