Electronics Forum | Thu May 30 10:31:03 EDT 2002 | robbied
Hi Yannick. This is an issue that we are just recently getting into but here is some ifo that I have gathered so far. I have seen/ used 2 different rework machines. The one we have bought is a 'PACE TF2000' which was at the lower cost end of the mar
Electronics Forum | Wed Mar 04 22:57:05 EST 2009 | davef
Underfill epoxies may be classified into major groups [Capillary Underfill Manufacturing Development and Characterization for 2nd Level Electronic Interconnect Processes; B Salom�n; University of Puerto Rico, Mayaguez Campus; Dec 2004]: * Capillary.
Electronics Forum | Fri Aug 26 09:57:21 EDT 2005 | russ
The Immersion gold is not a problem with BGAs specifically but "black pad" which can be present anywhere. The unfortunate thing with BGAs is you cannot see it. Personally I hate white tin. It is okay for single sided boards running no-clean, but c
Electronics Forum | Tue Sep 18 15:35:23 EDT 2001 | jschake
A laser cut stainless steel stencil was used exclusively for the evaluation of the complete 0201 assembly process, which addressed printing, placement, and reflow. However, I have also conducted off-line 0201 print tests using a nickel electroformed
Electronics Forum | Thu Jul 06 13:36:37 EDT 2006 | SWAG
We've had much trouble with flex circuits. As previously mentioned, you must have local fids for the board or the BGA itself (if panelized). Other troubles we experience are drilled holes for pinned connectors. Unless the PCB manufactur has some w
Electronics Forum | Tue Nov 28 21:16:17 EST 2006 | davef
J Rose at EMPF says: The introduction of no-clean solder fluxes in electronics manufacturing has given rise to greater levels of solder balling simply because the opportunity to remove them in the wash process does not exist. They are typically cause
Electronics Forum | Wed Dec 24 11:23:22 EST 2008 | childs
I can't seem to locate any information/concerns about moisture entrapment in IC packages on the promary side in a double sided SMT assembly using water soluable solder paste when soldering the second side. A typical process would assemble/reflow/cle
Electronics Forum | Mon Jun 19 09:47:23 EDT 2017 | georgetruitt
You have a lot to think about! What does the flux manufacturer recommend as far as specifics like water temp or pressure? Do they recommend high temp di-water a detergent or saponifier? Do you currently have a cleaning machine, batch cleaner or inl
Electronics Forum | Fri Jan 02 08:10:18 EST 2009 | childs
Thanks for the reply Stephen. The time factor sounds logical for moisture invasion during cleaning, probably why there's no articles showing concern about the process. I did try experimenting with some samples and believe it or not could not dupli
Electronics Forum | Fri Feb 19 14:43:46 EST 1999 | Nithy
We are in the process of getting into no-clean paste and fluxes. One important issue in this is sodler balling. I have heard some people say that having a matte finish would help in having lesser solder balls and that the solder balls would not be