On your question about reliability ... " Is there testing we can do (environmental stress chambers) with which we can see the long-term effects of flux residue on solder joints?" Sure, incompletely activated low residue flux residues are potentially
Electronics Forum | Thu Nov 02 13:17:06 EDT 2017 | jardcrocker
Hi...i have a question. After you solder a circuit board, what do you wash the flux residue off with? I am hesitant to use water for fear of subsequent corrosion, and have no clue as to what kind of flux is in my solder wire. automated pcb assembly
Electronics Forum | Thu Nov 02 15:45:04 EDT 2017 | dleeper
For low volume hand assembly, deionized water or IPA should work fine.
Electronics Forum | Tue Feb 11 14:05:11 EST 2014 | dontfeedphils
I can't speak too much as to why your joints are appearing dull, even with the booster. I can recommend a new chemistry that Kyzen has out that I've been running for about a year now. Price is about the same, it can be run at low(er) concentrations
Electronics Forum | Fri Nov 03 09:31:35 EDT 2017 | davef
On the flux reside issue that is gumming up your test probe pogos ... Short term, clean what's in process with a aerosol flux cleaner solvent. Ask your flux supplier for recommendations. Longer term, recognizing that there is no fix, your improveme
Electronics Forum | Tue Mar 05 03:58:10 EST 2019 | pcformax
Hello guys, In our company we use CS-FLUX for reballing purposes in the last two years and we have no complain about the product.if you want to see details about the product there is a very helpful tutorial in youtube named 'ATI GPU removal with the
Electronics Forum | Fri Nov 03 11:30:29 EDT 2017 | davef
regarding dwl comment, "For low volume hand assembly, deionized water or IPA should work fine." Deionized water: Deionized water is corrosive. It needs to be removed. Proof? Drop a copper coin into a covered jar of DI water and watch what happens ov
Electronics Forum | Fri Nov 03 15:43:20 EDT 2017 | dleeper
IPA and DI water are both very common and effective methods of cleaning PCBAs. http://www.zestron.com/sa/cleaning-applications/smt-electronic-cleaning/pcba-cleaning/aqueous-cleaning.html http://blog.gotopac.com/2010/11/18/ipa-as-a-universal-cleaner
Electronics Forum | Thu Sep 29 19:18:24 EDT 2005 | HLy
Hi, I noticed that the solder joints on my BGAs end up with a lot of wrinkles after reflow. See picture at: http://pstr-r02.ygpweb.aol.com/data/pictures/02/01A/17/DD/E3/9E/n8BhepQLFDs6GMSwaRNxPCTWR5NdpUJZ0300.jpg Does anybody have any ideas what cau
Electronics Forum | Fri Oct 07 09:19:54 EDT 2005 | Kris
the direction in which the solders cool in a BGA are also different than the rest of the boards as the joints " hidden" to ambient. Refer to an analogus phenomenon in the cookson application note. http://www.cooksonsemi.com/pdfs/How%20&%20Why%20Bum