Electronics Forum | Wed Nov 17 11:20:23 EST 1999 | Dave F
Hey Gyver: If you don�t mind (which you don�t have any choice about, because I�m going to do it anyhow, cause it�s MY word processor), I�m going to respond genericly, but still be directed to your question. Much of the following is paraphrased from
Electronics Forum | Thu Apr 22 18:07:38 EDT 1999 | Tom B.
| On various PCB's after building processes,such as reflow, flowsolder and wash. The soldermask on the PCB's have become discoloured, like a 'marble' effect all along the solder side of the board, it is lighter in contrast than normal, although when
Electronics Forum | Thu Apr 22 20:26:39 EDT 1999 | Dave F
| | On various PCB's after building processes,such as reflow, flowsolder and wash. The soldermask on the PCB's have become discoloured, like a 'marble' effect all along the solder side of the board, it is lighter in contrast than normal, although whe
Electronics Forum | Fri Mar 13 17:09:49 EDT 2009 | kmorris
We have found very small solder deposits on the gold fingers of some PCI boards after assembly at our CM. In the IPC-A-610, it says that no contamination or solder is allowed in the critical contact area. 1. I'm looking for feedback on what others
Electronics Forum | Thu Aug 28 23:15:44 EDT 2014 | phyllishwl
Hi all, Our production reported that they found 3 panels out of 53 panels with strange phenomenon after reflow. 1/ Blister / Delamination of PCB panels, 2pcs blister/delamination under solder mask, 1pc under Gold plating at Gold finger 2/ Silkscr
Electronics Forum | Tue Apr 23 15:36:27 EDT 2019 | davef
Josh, are you setting someone up with these questions? Answers to your questions related to the subject line follow: Q1. Does the Epoxy Solder Mask Layer of a PCB protect against moisture absorption? Is this a primary function of the solder mask?
Electronics Forum | Fri Jun 18 13:48:37 EDT 1999 | Earl Moon
| We currently use HASL on all of our boards and I would like to move to something else. I have sampled some boards with Entek OSP and I loved it, the problem is we have plated mounting holes on just about every board we make. Does anyone have info
Electronics Forum | Fri Aug 29 09:39:08 EDT 2014 | rgduval
I'll try to deal with the issues as you've presented them. 1. Blistering/delamination, shown in photo 2. The most likely cause of blistering/delamination like this is moisture in the boards. The moisture can get into the boards in multiple ways..
Electronics Forum | Tue Jun 02 08:30:30 EDT 1998 | Jon Medernach
I have to agree with Steve. If the problem is progessively worse the problem is the pitch conversion that was used, and I have seen it before. It may be masked by the solder paste which could be on pitch but after reflow the paste wickes to the pad
Electronics Forum | Sun Jun 13 05:46:21 EDT 1999 | Brian Ellis
Murray "No-clean" fluxes/pastes should not normally give "white residues". Before exploring cleaning, which is costly for small production levels, I suggest you may care to find out why you have these residues. To help you, can you please answer th