Electronics Forum | Thu Dec 13 08:02:02 EST 2007 | realchunks
You may want to try raising your pre-heater if you have one. I would also suggest trying different fluxes that may be a little more active so you can use less. What type of fluxer are you using? Selective solder flux residue is a gray area. This i
Electronics Forum | Fri Jul 23 14:41:41 EDT 2004 | Steve Stach
Dear JSK, It sounds like the root causes of your problem are two fold. First, excessive heat will polymerize the abietic acid found in rosin forming neo-abietic diamers and polymers which are much less soluble than the parent monomer. There are
Electronics Forum | Wed May 19 11:01:17 EDT 1999 | Vince Whipple
Wes, I have been involved with many customers changing over from an alcohol based no-clean to a VOC-free process. The change-over can be made easier by such things as air movement, convection preheat, "drains" or reliefs in pallets (if used), contr
Electronics Forum | Wed Jan 14 06:42:38 EST 2004 | tommy
We see spattered(spitting of flux or solder to nearby area) solder/flux on gold fingers.We view the gold fingers area under 30x before reflow and it is cleaned but after reflow we see flux droplets or solder on gold fingers. We tried to changed a new
Electronics Forum | Fri Oct 10 05:04:26 EDT 2008 | bing007
We are using Mulicore MF101 flux and a Vitronics selective soldering machine on a lead-fee assembly and are having trouble with nozzles blocking even when the nozzle aperture is increased. Has anyone come across this problem before using fluxes with
Electronics Forum | Wed Apr 03 04:08:20 EDT 2013 | ericrr
Yes well, now we used to add a bit of flux to our leaded paste to make it slightly runny, But when we went to unleaded paste the joker who came in from another company to set the temperature on the oven said "you dont add anything to unleaded paste!.
Electronics Forum | Mon Jun 19 09:47:23 EDT 2017 | georgetruitt
You have a lot to think about! What does the flux manufacturer recommend as far as specifics like water temp or pressure? Do they recommend high temp di-water a detergent or saponifier? Do you currently have a cleaning machine, batch cleaner or inl
Electronics Forum | Thu Jan 27 14:49:53 EST 2000 | Glenn Robertson
Tuan - One of the reasons I suggested pre-tinning (aside from the negative effects of Gold on appearance and reliability) is the known slower wetting of Sn/Ag and Sn/Cu alloys as compared to Sn/Pb. If you don't have to be Lead-free, the high Lead
Electronics Forum | Fri Feb 24 02:04:50 EST 2017 | soldertraining
Selective Soldering Frames can pull large amounts of heat from the solder wave at the point of contact, effectively lowering the temperature of the solder at the solder joint. You should confirm the temperature of the solder joints by running a therm
Electronics Forum | Wed Apr 11 22:05:58 EDT 2001 | davef
OA pastes are more hydroscopic than NC pastes. Hydroscopic. The capacity of a material to absorb and retain moisture from the ambient air. Sometimes this is compounded if you remove paste from the frig and let it warm to room temperature, because