Electronics Forum | Mon Jul 20 04:37:23 EDT 2009 | jdumont
We have used some sealed steel cabinets and a nitrogen generator (Balston 75-79 model) for about a dozen years with no issues at all. Humidity levels average 1% - 5%. We also just bought a couple of XDry (Totech) desiccant cabinets (XD2-1104-02) for
Electronics Forum | Wed Jul 08 00:16:30 EDT 2009 | magnifico
Hi Daxman I have the F4G installed in a host PC. I would like a summarized procedure (e.g. step 1, step 2, etc)on how to program, as reading from the manual is taking time. This could get me started faster. Appreciate any inputs. Thanks
Electronics Forum | Mon Jul 13 07:10:17 EDT 2009 | hcarrasco
1.- If you are using polyurethane squegges , they ned to be changed. 2.- Verify your printing parameters of pressure & Speed , It seems that your pressure & speed are high. 3.- If you are seeing excess in one side and insufficiency in the opossite
Electronics Forum | Thu Jul 09 08:14:48 EDT 2009 | rway
We are looking into purchasing a Falcon ICT/FCT from Digital Test. Does anyone have any experience with this company or the machine? 1) How would you rate their technical support? 2) What are the functional test capabilities of their machines (pr
Electronics Forum | Mon Jul 13 11:34:44 EDT 2009 | snsmt
thanks everyone! When we have a PCB to do, for one component, they usually give us an excess of 10 components! We are issued over 2,000 components. Does that sound reasonable? The problem is usually when the head picks up the component before it r
Electronics Forum | Sat Jul 25 20:53:14 EDT 2009 | mika
Author: Jeff Subject: DEK SMEMA to UIC Conveyor Instead of using a conversion box just make your own cable. Look in the Dek manual, volume #2, chapter 18. It shows you how it's wired. Easy to make and looks allot cleaner than those conversion box
Electronics Forum | Tue Aug 11 19:46:34 EDT 2009 | padawanlinuxero
Guys I have a question since the ever present problem with the crack switch we had to change to a low temp lead free solder paste in these case eutectic 58Bi/42Sn and 57Bi/42Sn/1Ag alloys, now the main question whats diferent between these one and th
Electronics Forum | Wed Sep 02 19:08:45 EDT 2009 | jlawson
Also consider electroltyics as some brands can only cope with one pass through reflow, 2 max. In Vapor phase 1 pass max is typical. Although depends on makers specs and what they say the device can withstand. main issue is Dielectrics get damaged , c
Electronics Forum | Mon Nov 09 12:12:41 EST 2009 | mcmark
Same here, I've been programming Mydata placement machines using CircuitCAM since 1999, at 2 companies. With an ASCII CAD file imported and simple BOM scrubbing, we can get programs directly output to our Mydatas in less than 5 minutes. Developing as
Electronics Forum | Tue Sep 22 08:35:47 EDT 2009 | cman
Did you try pre-tinning your board on this suspect pad/s to see if it improved wetting/solderability prior to printing/SMT placement and reflow? Does the pad/s not soldering tie to a ground layer? I would connect a T/C to each pad of the same part an