Electronics Forum | Thu Jun 06 15:18:56 EDT 2019 | gregoryyork
Honestly, If I ever have an SMT problem it's when a profile is at 230-235C. We encourage minimum 240C and typically 245-250C. Many components call for 260C. Some Paste manufacturers advocated 230C in the early years of Lead Free and it was a disaster
Electronics Forum | Fri Jun 07 09:39:06 EDT 2019 | cristian_amlima
I totally agree with you when whe talk about a lead-free process. In my early comment I thought we were talking about a tin-lead process with the pcb pb-free, when the solder paste limits should be respected. That is the motive the temperatures I sa
Electronics Forum | Mon May 13 08:31:48 EDT 2019 | robl
Do you have in line 3D Solder Paste Inspection machines? If not the 2D inspection on the SP710 is very slow & not a patch on Hawkeye from DEK. If print time is not an issue then it doesn't matter. I have had both types of machine, and personally pre
Electronics Forum | Mon May 13 06:38:41 EDT 2019 | relaycz
You need to give us a little more information. 1. What is the size of your panel? 2. Are there any heavy components? 3. What is the thickness of your board panel? 4. What kind of oven are you using? 5. Is it only a recent problem or ongoing one?
Electronics Forum | Mon May 13 23:44:26 EDT 2019 | dami0629
if use tray cannot solve the problem, you can change from the design 1）Reduce the effect of temperature on PCB 2) PCB USE HIGH TG 3) BOARD THICKNESS TOO THIN 4) MODIFY THE BOARD SIZE 5) Reduce the V-CUT depth.
Electronics Forum | Mon Jul 01 09:33:08 EDT 2019 | dbuschel
if you can't change the PCB materials or design at this point, you might be able to reduce it somewhat through the use of fixtures or edge stiffeners. Unless it is a particularly thick board, I don't think the reflow profile would be the issue. The t
Electronics Forum | Tue May 14 05:35:16 EDT 2019 | spoiltforchoice
You'll be lucky if there is I would guess. I think two places tried and failed to sell them in the UK and it looks like Manncorp gave up in the US too? Presumably that means they primarily exist in asian markets where they have some niche application
Electronics Forum | Fri May 31 12:28:45 EDT 2019 | slthomas
You really need to define what you mean when you say "bend" and when you say "break". You might have zero damage to a bare board but cracked solder joints and ceramic caps on an assembly, given the same amount of bending or stress. It all depends on
Electronics Forum | Sat Jun 01 01:15:52 EDT 2019 | dhanish
Thanks Steve.The bent we are seeing is at the location without any component .It is a small and long pcb,one side fully loaded with component .Thebother side got no component. We can manually bend the pcb at the side without the component. All the la
Electronics Forum | Tue May 21 16:48:29 EDT 2019 | Matt
Hey, thanks for your feedback, this was our initial thought however our process engineers don't buy this. Although they are close to the card edge this product only has de-panel length wise which is perpendicular to these capacitors. The PCB its