Electronics Forum | Mon Aug 13 09:49:35 EDT 2012 | rjlatz
I just got back from a visit to our PCBA manufacturer. We have good flowthrough on the PTH, but solder skips and bridges on the SMT SO IC's. We have correct orientation and robber pads, but the results are still the same. I noticed the wave shape is
Electronics Forum | Tue Aug 22 16:02:07 EDT 2000 | Dr. Ning-Cheng Lee
If the thermal mass of the products is small, a tent-shaped profile is recommended, with peak temperature around 240C. The hottest spot on board should be less than 250C. However, if the thermal mass of the product is large, such as a large server PC
Electronics Forum | Wed Mar 10 13:53:13 EST 1999 | Vincent Vega
| We will wave solder a board with SOIC14 and SOIC16 parts on the bottom. It has been difficult to find any specific wave solder process recommendations from manufacturers of the SOICs. The pad geometry utilizes theiving pads on both sides to reduce
Electronics Forum | Thu Mar 25 19:07:22 EDT 2021 | llawrence
That is all a lot to take in, but thank you all for the recommendations. From what I understand, I'm going to start by ordering a new polished 0.1mm stencil with size reduced apertures and seeing if reduced paste deposit will help. As for the sten
Electronics Forum | Tue May 17 08:00:26 EDT 2005 | Bob R.
We went through this with one PBGA supplier recently and they were able to get the problem under control by fixing some of their molding processes that were inducing residual stresses. You can really see it in a thermal moire where you measure warpa
Electronics Forum | Tue Aug 18 10:17:15 EDT 2009 | grantp
Hi, You don't need X-ray and all that crap. I would get an old MYDATA TP9 or something like that, and a manual stencil printer and a batch oven or a small inline oven. Should do the trick and be very low cost. Should be simple to use as well. Tha
Electronics Forum | Tue Aug 11 17:36:44 EDT 2009 | dyoungquist
You are looking for a complete SMT assembly line plus possible X-Ray inspection and rework equipment. The 3 components of the SMT line are stencil printer, pick-n-place machine and reflow oven. How small are your components? 0603? 0402? What is the
Electronics Forum | Tue Feb 16 16:28:30 EST 1999 | Tuffty
| | Can anyone help me with the pros and cons of trying to wave | | solder tantalum and large (1812) ceramic capacitors. I do | | know that one may see fractures on larger cermaic caps, but have not seen much on the tantalums. Any insight as to what
Electronics Forum | Thu Jul 03 03:23:04 EDT 2003 | loz
I have been advised recently about pcb manufacturers, that somehow or other supply pcb's with contamination. Visually they are fine, but problems arise during SMT manufacture, ie solder balling, non-wetting on pads, and also during wave solder proces
Electronics Forum | Tue Nov 12 17:11:32 EST 2013 | mondalaci
Hi Folks, I'm working on a LED display that is composed of multiple layers. What is interesting for the point of this discussion is the PCB layer and the light deflector layer on top of it. Please take a look at the related pictures at http://plus