Electronics Forum | Wed Dec 14 12:51:47 EST 2005 | grantp
Hi, Cool, I did not notice your last post on this thread, and I will check out your results, as I am not convinced about batch convection, but if you've cracked it, and have a stable product, it's very good to know. Regards, Grant
Electronics Forum | Thu Nov 10 04:02:25 EST 2005 | Rob
Did you ever think that if you American's hadn't been in such a rush to get there ahead of the commies in the first place, perhaps he'd be bothering them now instead?
Electronics Forum | Tue Nov 22 09:52:57 EST 2005 | moonshine
Might be resin smear. Check out all the stuff on my free site as articles, photos of almost every board defect imagineable plus much more. Did I mention, It's ALL FREE ALL THE TIME? MoonMan
Electronics Forum | Tue Nov 22 10:46:56 EST 2005 | Rob
No, come to think of it I don't think you did. Well, at least if you discount the last 5000 times. Sorry, I'm exaggerating only 4952 times. ;0)
Electronics Forum | Wed Nov 23 15:43:04 EST 2005 | Samir
Moonman, You never did answer the question. Was that you in the green smock and your finger pushing the button?
Electronics Forum | Tue Nov 29 08:32:08 EST 2005 | stefwitt
Particular as a small company and limited resources you�ll be requiring a lot of assistance from the machine vendor. Did you check which other machines are used in your area and if there is already a local service tech? Did you get in contact with o
Electronics Forum | Thu Nov 24 05:56:32 EST 2005 | mskler
We are using QFP & other IC's in SMT but not using the antistatic pecautions. I want to know that what effect can be on IC's in future. Because we did not get any IC damege immidiatly. How long after this will affact the IC,s.
Electronics Forum | Tue Dec 06 14:56:46 EST 2005 | bigdaddysoy9
Did you update the configuration for the new camera? After changing the configuration I think you have to power cycle the machine for the new settings to take effect.
Electronics Forum | Thu Dec 08 08:18:29 EST 2005 | grantp
Hi, We have recently moved to flash gold as well, as we had solderability issues with emerson gold, and this was supposed to be a solution. However I did not know flash gold would be thicker, and could have other issues. Is flash gold a stable boar
Electronics Forum | Mon Jan 09 11:26:08 EST 2006 | abhinavajmera
Dear Grant, Thank you for the reply. It is really a valid reason and I did check for it but nothing turned out that way. Can you think of some other reasons if the process parameters are the same used earlier when there was no problem at all. Regard