Electronics Forum | Fri Jul 22 03:07:45 EDT 2005 | Joseph
Dear all, As we know there is a high risk of reliability issue due to lead contamination during mixture of NLF component at LF wave soldering process. But we have the following feed back from one of our customer as follow: Concerning the risk of m
Electronics Forum | Sat Jul 26 12:04:32 EDT 2008 | davef
Services, Recycling, Electronic boards * American Scrapmetal; 7120 Rufe Snow Dr, Suite 106-184, Fort Worth, Tx 76148; 817-891-5297 americanscrapmetal@hotmail.com http://www.americanscrapmetal.com * Clean Harbors, Inc; 1501 Washington St, PO Box 8590
Electronics Forum | Mon Feb 20 23:01:05 EST 2012 | davef
Services, Recycling, Electronic boards * American Scrapmetal; 7120 Rufe Snow Dr, Suite 106-184, Fort Worth, Tx 76148; 817-891-5297 americanscrapmetal@hotmail.com http://www.americanscrapmetal.com * Clean Harbors, Inc; 1501 Washington St, PO Box 8590
Electronics Forum | Fri Sep 17 09:54:40 EDT 1999 | Brian
| | | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a
Electronics Forum | Fri Sep 17 10:09:17 EDT 1999 | Earl Moon
| | | | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However,
Electronics Forum | Mon Feb 25 21:13:12 EST 2002 | davef
No, none of us can tell you what is the acceptable level of halide content or contamination in flux residue. The level of harmful residues on your product helps determine the reliability of your product. We know nothing of your product, its custome
Electronics Forum | Fri Jun 01 16:22:35 EDT 2001 | davef
Your supplier�s approach to managing process change is TOTALLY UNACCEPTABLE!!!! Now, let me get the froth back in my mouth. How in the world do we know if the residues on these "no-clean" boards are compatible with your product? J-STD-001C, para 4
Electronics Forum | Thu Aug 19 12:14:22 EDT 1999 | Doug Nebel
| OK folks, let's get real serious. | | Well, I shot off my big mouth yesterday during a scheduling meeting concerning DFM and rework. Again, what an irony, oxymoron, or that other thing. | | Anyway, I said it would take another 4 weeks to develop
Electronics Forum | Thu Jan 05 16:39:47 EST 2006 | pjc
Electrovert has a new nozzle design called UltraFill. It was designed specifically for Pb Free applications and generates about 40% less dross than the previous Lambda design. UltraFill can of course be used for Sn/Pb alloys. The name UltraFill is fo
Electronics Forum | Tue Jun 13 10:23:54 EDT 2006 | patrickbruneel
Hey Rob don't give up yet let your voice be heard, the fat lady didn't sing yet!! Grant, you wrote "I think it's easy to be pro RoHS because you have to accept it, and implement it, however it's still nice to complain." You don't have to accept any