Hi! Mike My company is using the electric dry box and it can controlled less than 10% within 2.5 hours if we are not going to open the door. In normal working environment and it still can't control around 30%. Is it something that you are looking
Electronics Forum | Fri Feb 20 09:31:02 EST 1998 | Chrys Shea
| Can anyone tell me any posible ways to help cut down on solder dross in an inert environment wave???? Any suggestions would be helpful. It depends on how the environment is inerted. Is it a hood, tunnel, or boundary (Electrovert Contour) system?
Electronics Forum | Wed Mar 24 16:50:08 EST 2004 | davef
RA and RMA flux residues are "sealed" in a hard, glassy coating that do not require cleaning in many end-use environments. That being said, automotive, automotive underhood, and deep well are in that [ascending] order the three most burtal environme
Electronics Forum | Thu Aug 10 06:33:59 EDT 2006 | saaitk
Can anyone advise if there are any industry standards for SMT Environments. I am setting up an SMT area in a new facility and need to know about temp, humidity, filtration levels etc.
Electronics Forum | Mon Jun 30 15:47:46 EDT 2014 | AK
Thank you SteveO, I have also tried reflow 2nd time without any problem, but I also do not know the impact of long term reliability as our devices are most likely operated in the harsh environment. We are currently do soldering in Argon environment.
Electronics Forum | Tue Jan 08 08:52:30 EST 2019 | ameenullakhan
Hi Steve, We did the below trials today. 1. Run the board in O2 environment. result : Yellowish appearance was observed. After DI water Cleaning : Still the yellow color is there. 2. Same board run secondary side. Result : First side board yel
Electronics Forum | Thu May 18 09:17:04 EDT 2000 | Hella Electronics Corporation
Is it possible to print, place and reflow punch and return style boards in a high production environment
Electronics Forum | Thu Jun 23 12:29:05 EDT 2005 | davef
Look here: http://www.esd.tv/pdf/Cleanroom_Environments.pdf
Electronics Forum | Wed Oct 25 15:11:53 EDT 2006 | bobpan
Now that is a tough question to answer!!!!!!
Electronics Forum | Fri Jan 30 06:20:43 EST 2009 | milas
Hi Does anyone have any thoughts on Lead Free solderjoints reliability in a high vacuum environment ?