Electronics Forum | Tue Mar 21 18:52:45 EST 2006 | GS
Ahoj Pavele, di you considered to try a Type-3 solder paste ? Best Regards...........GS
Electronics Forum | Mon Apr 24 20:02:38 EDT 2006 | evsint
Why don't you guys look at the "WORLD LEADERS IN SOLDER RECOVERY". EVS International make the EVS 3000 and EVS 6000 Solder Recovery Systems. Many other companies have tried to come up with different ways of recovering solder but the EVS is the best
Electronics Forum | Wed May 17 12:22:09 EDT 2006 | russ
What color is the pad? coated with solder?, black?, still gold? Russ
Electronics Forum | Wed May 17 12:31:54 EDT 2006 | Mark
Hi , It looks like there is solder (shiny like mirror surface). Defently not black and not gold. Regards Mark
Electronics Forum | Thu May 18 10:28:46 EDT 2006 | slthomas
Are you seeing added solder or is it possible you're looking at nickel?
Electronics Forum | Wed Jun 07 22:02:57 EDT 2006 | davef
Similarly, we have eliminated solder balls by using an aqueous washer.
Electronics Forum | Wed Jun 21 13:23:45 EDT 2006 | russ
You may want to pre tin wires then dip into flux before soldering Does work!
Electronics Forum | Wed Jul 05 09:00:13 EDT 2006 | russ
Sounds like possibly too little preheat. Russ
Electronics Forum | Tue Jul 11 11:24:29 EDT 2006 | russ
30 gage wire and lap solder, you will have no issues.
Electronics Forum | Thu Aug 24 14:42:30 EDT 2006 | any
y we had solder ball after reflow owen?