Electronics Forum | Tue Apr 19 09:13:49 EDT 2005 | bobpan
Try printing while the paste is cold.....you get nothing but bad prints!!!!
Electronics Forum | Thu Apr 21 04:16:17 EDT 2005 | Infinity
Dear all, I am doing some small business selling solder paste, chip capacitors and resistors in China. I am going to expand the existing SMT product line. Can you experts throw in some ideas? For example, what other products would you all think of
Electronics Forum | Fri May 20 14:43:38 EDT 2005 | jfullerton
billscheu wrote: "just use 63 37 solder for repair. I do not know of any specification which prohibits this and until the people who create the rules change them this is the best." All due respect, but do you know what RoHS is? If you sell product i
Electronics Forum | Thu May 05 14:08:51 EDT 2005 | patrickbruneel
Ken, I bet ya the machine is so fast it produces enough heat to solder the parts when placed
Electronics Forum | Tue May 03 07:44:45 EDT 2005 | mmjm_1099
Try this: http://www.smtnet.com/forums/index.cfm
Electronics Forum | Mon May 09 17:27:46 EDT 2005 | cmiller
They are expensive so you need to have a lot of jobs that take a long time to hand solder or have a ton of masking. Also look at bottom side wave soldering, if you are having a lot of defects, the selective will allow you to solder both sides in surf
Electronics Forum | Wed May 04 10:44:55 EDT 2005 | russ
What exactly what "Ghastly" about it?
Electronics Forum | Mon May 09 15:21:28 EDT 2005 | tforbes
Hello, I am hoping that someone can shed some light on my somewhat strange question. The group that I recently started with have had a process in place where they do not run crystals through their wave solder process. From my previous work experien
Electronics Forum | Thu May 19 07:06:59 EDT 2005 | py
have you some GND layer inside the pcb ? see IPC 610 A
Electronics Forum | Fri May 20 10:54:04 EDT 2005 | cyber_wolf
We agree with Locutus F.