Electronics Forum | Mon Aug 18 11:20:08 EDT 2008 | pjc
Stencil apertures are cut to deposit solderpaste onto the annular ring, provided its wide enough. Then you can place a solder preform if needed to ensure there is enough solder to fill the barrel. Here is some information on solder preforms: http://
Electronics Forum | Wed Jun 29 12:31:32 EDT 2022 | proceng1
I don't know about that paste, but I can give my experience trying intrusive reflow (pin in paste). Using standard Lead-Free paste, we often had issues. It seems that many ROHS parts can't actually handle reflow ROHS temperatures. So the fact that
Electronics Forum | Mon Dec 11 20:44:37 EST 2006 | davef
Title : LEAD-FREE WAVE SOLDER FLUX EVALUATION Author : Michael Havener Author Company : Benchmark Electronics, Inc Date : 09/25/2005 Conference : SMTA International Abstract : The European Union�s deadline to ban lead in electronic pr
Electronics Forum | Mon Oct 15 14:36:03 EDT 2018 | davef
The methods of verifying PTH hole-fill. 1 Visual inspection 2 x-ray inspection works very well for inspecting such a connector for voiding and hole fill. View the connector off-vertical, at between 30 and 45 degrees. As always, the solder connect
Electronics Forum | Thu Sep 30 12:29:01 EDT 1999 | Dave F
| Hi everyone, | | Greetings! | | I�ve got a 2-layered through-hole PCB�s having the following problems: | | Solder Mask peels after wave soldering at random locations and only at the bootom side of the PCB | Insufficient Solder and some solder ne
Electronics Forum | Thu Sep 30 21:37:44 EDT 1999 | Dreamsniper
| | Hi everyone, | | | | Greetings! | | | | I�ve got a 2-layered through-hole PCB�s having the following problems: | | | | Solder Mask peels after wave soldering at random locations and only at the bootom side of the PCB | | Insufficient Solder an
Electronics Forum | Wed Feb 20 15:20:34 EST 2013 | hegemon
Depending on your requirements, you could range from a hair dryer, heat gun, toaster oven, hot plate, on up to digitally controlled surfaces and convective systems. You'll have to gauge for yourself whether you are just trying to add some heat energy
Electronics Forum | Wed Jun 08 17:35:04 EDT 2016 | slthomas
We all know that whenever possible, we want thermal relief between the barrel/pad and the copper foil to make it easier to properly solder that through hole connector. My question is, assuming there is no connection from the barrel to a copper layer
Electronics Forum | Mon Nov 01 17:13:37 EST 1999 | Mark W.
Jason, What is the revision of IPC you are referring too?? IPC 610 rev. b requires 75% fill on classes 2 & 3. Class 2 does allow the exception of 50% fill if the PCB has a Metal Core or Thermal/Heatsink Plane provided that the solder extends 360 de
Electronics Forum | Thu Sep 02 15:51:15 EDT 2004 | cburress
All: IPC does not directly state any criteria for physical characteristics of what a filled via should look like when embedded within a surface mount component's pad. I am using several of these in my design, and have received PCBs that exhibi