Hallo Joanne, I had employed by producer of Ecofrec 303. We make many tests of corrosion and conductive test in our company. All results of this tests was OK . Vast majority correspond mil standarts. When I ask my labor assistent in BRY, white residu
Electronics Forum | Mon Jan 10 18:35:05 EST 2011 | eadthem
Ive used a Mirtec machine for 3 years MV3L with side angle inspection. Mirtec has some issues documentation, and repair plus. But there machine is impressive and the AOI software is good. We can find about 90-99.99% of all errors using just the 5
Electronics Forum | Fri Feb 20 13:01:26 EST 2004 | Jay
First, it depends on the alloy composition of the solder. As you might know, eutectic Sn/Pb solder has the lowest melting point among available conventional solder systems. (except those based on Sn-In and Sn-Bi systems.) For example, 63Sn/37Pb - 183
Electronics Forum | Tue Jan 16 07:59:36 EST 2007 | tk380514
we worked out that the wave soldering cassettes Duratstone material takes alomst 35 degree away from the surface of the pcb, and the speed is already too slow it should be over 1.0 - 1.8 meters a minute but its now already 82 cm a minute, in order to
Electronics Forum | Mon Apr 08 14:16:29 EDT 2019 | sever_83
We've never heard of seen of such a thing either. We tried a clean sample board and applied con coat. Same process through out and we saw nothing. After speaking with the original operators who was curing the boards he had left the boards much longer
Electronics Forum | Fri Jun 29 14:15:00 EDT 2001 | stefo
This is a question about complying with J-STD-001 solderability testing. Do any of you have your vendors certify that the components and PCB's that you buy from them comply with the solderabilty requirements spelled out in the -002 and -003, in lieu
Electronics Forum | Fri Jun 19 14:25:24 EDT 1998 | Earl Moon
| | Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | | Mike | There has b
Electronics Forum | Fri Jun 19 13:40:25 EDT 1998 | Terry Burnette
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike There has been a
Electronics Forum | Tue Mar 14 07:59:41 EST 2000 | JAX
Emmanuel, The discussion on what finish to use whether it be HASL, Immersion gold over nickel, Organic Solderability Preservatives, ect...... is still ongoing. This is not the only decision you need to make. Do you plan on Soldermask Defined Pads? Wh
Electronics Forum | Tue Mar 14 07:59:41 EST 2000 | JAX
Emmanuel, The discussion on what finish to use whether it be HASL, Immersion gold over nickel, Organic Solderability Preservatives, ect...... is still ongoing. This is not the only decision you need to make. Do you plan on Soldermask Defined Pads? Wh
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830