Electronics Forum | Fri Mar 02 19:30:08 EST 2007 | Aquino
Yes, our company is also using SCS7 at the moment. Price is really cheap compared to all other solders. So far, we have been using it for about 1 1/2 years, no problem at all!
Electronics Forum | Thu May 25 19:21:58 EDT 2006 | grantp
Hi, So that's really important to have a specific flux for lead free? We are looking at changing to SN100C after reading this thread and other stuff we have found, so can anyone recommend the best no clean flux for that metal? Do you need differen
Electronics Forum | Fri Dec 30 10:12:27 EST 2005 | Cmiller
Joseph, thank you for your comments. Can I ask what kind of flux you are using?
Electronics Forum | Sun Jan 01 21:02:54 EST 2006 | sumxp
Please elaborate more on hole fill issue.How difficult to optimise the process para?
Electronics Forum | Fri Mar 31 15:49:51 EST 2006 | GS
Hi Marcus, by using SN100C have you seen any tearing phenomena like what shown on the link ? http://www.smartgroup.org/pdf/Defect01.pdf Tnks Regards.........GS
Electronics Forum | Mon Apr 10 13:10:06 EDT 2006 | Marcus
No I have seen Zero hot tears. Thats with water soluble or No-Clean. We have built over 10,000 boards.
Electronics Forum | Thu May 25 18:59:12 EDT 2006 | Tony S.
We are using the Kester 979 with excellent results; the bonus is that it can be cleaned w/Di water.
Electronics Forum | Fri Apr 04 09:54:39 EDT 2008 | redtiger56
We have been seeing continued difficulty with solder shorts and/or insufficient barrel fill with our Juki selective solder machine while using SAC305. We want to switch to something in the SN100 series, but we do not know enough to seperate the hype
Electronics Forum | Fri Mar 31 12:27:27 EST 2006 | Marcus
We have used the SN100C for over a year now with fanastic results. We use the SAC305 for SMT and SN100C wire exclusively. There are no problem mixing the alloys. I am also on the commitee for the NASA testing. The SN100C did out perform SAC and SnPb
Electronics Forum | Sun Jan 01 22:48:46 EST 2006 | Joseph
We are using selective soldering pallet, which the soldering flux is Interflux 2005M. We encountered the poor hole fill mainly at the heat sink components. Initially we tried to apply more heat but tend to overkill the flux activity. After some modif