Electronics Forum | Mon May 24 04:01:10 EDT 1999 | Joe Manzur
John, We are using a well known solder paste, begining with the letter "H". (I don't want to be accused of advertising). Also, we are now using a board inverter. In the early day's however, before we purchased a board inverter, we were having to
Electronics Forum | Mon May 17 10:17:23 EDT 1999 | Chrys Shea
| Hi Chrys! | | I've also heard stories of the water-based material "attacking" the inner workings of their spray nozzles - probably due to the water hanging around parts and corroding them. | | Did you have any such problems with the USI ultrasoni
Electronics Forum | Thu Apr 29 16:52:11 EDT 1999 | Steve Gregory
| | | | Has anyone heard of this company? We have one at our facility and I can't find them listed anywhere. I looked through this years NEPCON directory with no listing there either. We have some parts that need replacing so any help would be gre
Electronics Forum | Tue Apr 27 12:14:08 EDT 1999 | M Cox
Board Experts I am fighting with a board house about a delamination problem.. First the facts 1) 10 layer board .063 thick HASL Finish Aprox 16 in x 17 in. 2) 150 Boards with this part number built with the same reflow oven settings (212 c max t
Electronics Forum | Sun Apr 25 12:05:50 EDT 1999 | Chrys Shea
| | | Has anyone had trouble waving and gluing 0603 R's and C's? At my company, our designers have "opened the floodgates" on bottom-side 0603's. | | | | | | We've got an EPK+ with rotary chip and omega wave but can't seem to get skip-free solderin
Electronics Forum | Mon Apr 26 09:18:27 EDT 1999 | C.K.
| | | | Has anyone had trouble waving and gluing 0603 R's and C's? At my company, our designers have "opened the floodgates" on bottom-side 0603's. | | | | | | | | We've got an EPK+ with rotary chip and omega wave but can't seem to get skip-free so
Electronics Forum | Tue Apr 20 23:18:48 EDT 1999 | KEVIN SIMPSON
25 PPM)! | | 1. Is there a better process to solder the leads of QFP's with lifted "minute" lifted leads still having a realiable solder joints? | | 2. Or has anybody tried modifying solder pads and use thicker solder paste deposit to compensate fo
Electronics Forum | Fri Apr 16 19:02:39 EDT 1999 | Dave F
| While trying to sell me a low temperature baking system for SMDs the salesman mentioned that the 125C for 24hr bake had been known to cause co-planarity defects. | I thought I'd ask some experts. Any help guys? | Gerry: I imagine there could be s
Electronics Forum | Wed Apr 14 20:39:02 EDT 1999 | Dave F
| I need to cure conformal coat on a 19" x 15" board. The material needs 7 - 10 minutes at 100deg C, but I have limited floorspace so I'm looking for an oven with about 36 inches heated length and 18 or more inch wide belt. The material we are consid
Electronics Forum | Sat Apr 17 11:56:04 EDT 1999 | Graham Naisbitt
Mike First, you MUST make sure the oven used is extracted. The coating will contain TDI. This is not nice. You would be better considering a silicone solventless. Try contacting HumiSeal. They had a material on the TAC line at Nepcon West that lo