Electronics Forum | Wed Sep 03 16:15:30 EDT 2008 | blnorman
Elemental is by SEM/EDX. The brown coloration does resemble the 3 micron photo. Again, if I'm picking up copper (our Ag plating thickness requirements are 0.05 micron to 0.12 micron following IPC 4553), maybe we do have a porous silver plating.
Electronics Forum | Thu Aug 24 15:54:13 EDT 2006 | davef
It depends. What is: * Storage environment and period * Board laminate, epoxy, and copper thickness of PTH * Down stream process * Etc FR4 0.062" thick boards absorb between 0.08 to 0.1%Wt of moisture within a 24 hour period, and 0.2 to 0.23%Wt in
Electronics Forum | Mon Jan 10 03:45:23 EST 2022 | proy
YES there is an IPC target/acceptable spec In general terms the barrel thickness in the hole should be 1 mil (thou). IPC has an allowable limit lower around .75 with some other factors. I have been checking barrel plating on all incoming boards since
Electronics Forum | Thu May 29 14:27:04 EDT 2003 | larryk
This flex is .001" Kapton polyimide. The flex portion of this rigid flex consists of 3 layers of 1 oz copper with 5 layers of Kapton. Part of the flex is sandwiched in standard FR4 with two layer of copper on each side for a finished thickness of .
Electronics Forum | Sat Sep 20 11:44:39 EDT 2003 | Gabriele
Few questions: - wich type of C-CGA ? (CAST or CLASP column to ceramic attach) - column pitch ? - column count ? - capped (with lid) ? or capless (c4 die on top)? - PCB board zize and thickness ? - PCB copper finisch ? (OSP,HASL, ENIG, etc) - v
Electronics Forum | Fri Jan 21 14:51:08 EST 2000 | Dave F
Mike: I�d hate to see you making design decisions, based solely on the discussion here, but that this would be an impetus to consult IPC-D-279, "Design Guidelines ... " and take a course on designing reliable boards. Werner Engelmaier (Engelmaier
Electronics Forum | Fri Jul 24 23:20:11 EDT 2009 | umar
Hi Dave, Thanks on your feedback, May I know the how's the contributing of Moisture content of bare board and the Thickness of the copper plating in the PTH to the solder ball and solder splash during hand soldering process ?
Electronics Forum | Fri Jul 30 14:50:26 EDT 1999 | Kevin Hussey
| I received a request from customer to assemble ceramic substrate (alumina oxide)that printed with a low temperature Copper thick film conductor (the overglaze layer is polymer). The Copper pads are exposed without any coating. | This ceramic substr
Electronics Forum | Fri Jul 30 16:02:49 EDT 1999 | Earl Moon
| | I received a request from customer to assemble ceramic substrate (alumina oxide)that printed with a low temperature Copper thick film conductor (the overglaze layer is polymer). The Copper pads are exposed without any coating. | | This ceramic su
Electronics Forum | Wed Mar 03 17:09:55 EST 1999 | Tom Reilly
We have recently had problems with bare boards coming in too thick. I would like to know how to properly specify the minimum and maximum thickness using the 13949F and IPC 4101 specs. (We currently use "MATERIAL: GFN 0620 C1/C1 A2A per MIL - P - 1394