Electronics Forum | Sat Sep 18 13:05:57 EDT 1999 | Brian
| | | | | | Dave, I'll respond by paragraph: | | | | | | | Brian: | | | | | | I like Ag2 also. I prefer it over both 63/37 and 60/40, if the price is not a factor. Yes, gold rips through eutectic and near-eutectic solders like habanero slath
Electronics Forum | Sat Sep 18 14:37:00 EDT 1999 | Earl Moon
| | | | | | | | | Dave, I'll respond by paragraph: | | | | | | | | | Brian: | | | | | | | | I like Ag2 also. I prefer it over both 63/37 and 60/40, if the price is not a factor. Yes, gold rips through eutectic and near-eutectic solders like
Electronics Forum | Wed Aug 15 16:04:23 EDT 2001 | davef
First, responding to your question � Several things on copper dissolution in solder are: * A 50um copper wire will dissolve in 60Sn / 40Pb solder at: - 200�C solder in 55 seconds; - 250�C solder in 20 seconds; - 300�C solder in 5 seconds; - 350�C so
Electronics Forum | Thu Dec 06 23:34:25 EST 2001 | Beny
Pls. help. I�ve problem with non-wetting defect at capacitor termination. I have faced this problem at the 2 kinds of termination. One is chip capacitor 0603 that its outer termination surface composed with 100 Sn (Lead free) and another one is Sta
Electronics Forum | Fri Jun 16 14:54:21 EDT 2006 | jbrower
Howdy Bolo, I see. I currently run a 5 zone 1500 Heller, It's a very nice reflow oven and one of my favorites. Hopefully in July we will be getting in our 1700 from Heller. These reflow ovens (used) can be had for a pretty decent price at least in
Electronics Forum | Thu Aug 06 19:20:09 EDT 2009 | boloxis
easy, just dip the ICs on a very weak solution of Nitric Acid, by very weak I mean like drops of Fuming Nitric acid in a half full DI water beaker. Place the beaker on a Ultrasonic bath and dip/shake the ICs in the solution in 5~ 10 seconds only. You
Electronics Forum | Fri May 07 17:38:00 EDT 2004 | bruce @ knoll
I will try that next. I did speed up the wave pump motor with a larger pully(20% more speed) This was done at the time to try to increase the size of the wave because I had component leeds touching the wave pot as they passed by. Due to the wave high
Electronics Forum | Tue Dec 16 15:43:26 EST 2008 | fctassembly
Converting your machine from lead to lead-free can be performed in a few steps: 1)Ensure the solder bath is up to temperature 2)De-dross the solder bath 3)Remove pumps/ flow ducts; etc. clean very well- set aside 4)Purge leaded solder 5)Remove as muc
Electronics Forum | Fri Jul 24 12:35:56 EDT 1998 | Russ Miculich
The variance of useability of any of the pastes with a difference of 5% in your overall environment will probably not even be measurable in the difference of the paste be it RMA, Water Soluble, or No Clean. What is the printer you are using and is i
Electronics Forum | Mon Oct 12 03:09:06 EDT 2015 | akon63
Problem with cleaning these machines is once you > start it's easy to get carried away. ;) > > We > cleaned our SPA-400F a few months ago, had been > offline for a while as we were using our > SPA-250. > > It started as just a clean and to > r