Electronics Forum | Wed May 03 13:06:54 EDT 2000 | Sal
GUYS SEEING A PROBLEM WITH SOLDER PASTE LEACHING. THE PCB IS HASL FINISH , AND THE DEVICE IN QUESTION IS A O.O30" PITCH RESNET. THE SIZE OF THE PADS ARE 0.020 x 0.0.047 THOU , THE APERTURE SIZES ARE 0.018 x 0.042 THOU . THE LEACHING IS OCCURING DUE
Electronics Forum | Tue Nov 04 12:58:17 EST 2008 | smt123
I have to agree with Patrick here. This image appears to show a board that is NOT HASL as there is what appears to be a copper pad in the upper portion of the image. But then again the arrow tip appears to be white and I woudl expect that to be red s
Electronics Forum | Wed Apr 07 08:28:41 EDT 2004 | Dougie
Hi, We are Scottish manufacturing company considering a move to Immersion Silver finished PWB's from HASL. The driver behind it being the RoHS and WEEE legislation in Europe at present. My question is... We plan on using a Sn/Cu/Ni solder bar in o
Electronics Forum | Wed Apr 07 08:30:22 EDT 2004 | Dougie
Hi, We are Scottish manufacturing company considering a move to Immersion Silver finished PWB's from HASL. The driver behind it being the RoHS and WEEE legislation in Europe at present. My question is... We plan on using a Sn/Cu/Ni solder bar in o
Electronics Forum | Tue Aug 22 14:59:55 EDT 2000 | Mike Naddra
What does the reflow profile look like , the question I had was surrounding the higher reflow temperature and the max temperature that lowest thermal mass components will see. Some other questions that I had were surrounding the components , what of
Electronics Forum | Tue Aug 22 16:02:07 EDT 2000 | Dr. Ning-Cheng Lee
If the thermal mass of the products is small, a tent-shaped profile is recommended, with peak temperature around 240C. The hottest spot on board should be less than 250C. However, if the thermal mass of the product is large, such as a large server PC
Electronics Forum | Thu Aug 06 17:25:55 EDT 1998 | Earl Moon
| Is there any problem using SMT on gold boards? 15 years ago we were told not to use gold boards, but I can't remember why. Judging by the other postings it now appears to be common. Only problem I see is that the nickel should be plated, not ele
Electronics Forum | Fri Jun 19 10:03:46 EDT 1998 | Earl Moon
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike Mike, We and ind
Electronics Forum | Fri May 28 16:30:39 EDT 1999 | JohnW
| Yes l know this problem keeps cropping up on the forum but l've missed some of the follow-ups. | | Our problem is that the lifting only occurs on 3% of production so actually detecting an improvement is difficult. We're actually having to inspect
| 1 |