Electronics Forum | Thu Jun 08 16:12:19 EDT 2017 | davef
Your plater's recommendation should work fine. Your simple copper plate will work, but you'll be stepping into fighting a copper tarnish battle. Silver over the copper is a better choice. I was thinking a silver thickness of a minimum of 3 microns
Electronics Forum | Thu Jun 08 18:19:40 EDT 2017 | edhare
Jeff, You might look at this paper, which has some background & references that are relevant to your question ... http://www.semlab.com/papers/diffusionbarrierplatinginelectronics.pdf Ed Hare
Electronics Forum | Wed Feb 03 18:36:47 EST 1999 | Earl Moon
| Does anyone know if I will have problems soldering surface mount components to an all hard gold plated PC board. We want to use hard gold similar to gold used for edge fingers because our customer is concerned about wear and conductivity of connect
Electronics Forum | Mon Mar 30 11:39:46 EDT 2009 | rgduval
Is this a sample board that you ran without components? If so, I'd get it back to your board house, and ask them to explain to you what's happening. We never did get to a satisfactory root cause on our issue (at least, satisfactory to me). It seem
Electronics Forum | Mon Jun 12 07:42:56 EDT 2006 | brian.perry@suntroncorp.com
We are placing a gold plated device (LCC) to a NiAu PCB using a SnPb No-clean solder. We're noticing quite a bit of difficulty with reliable joints (intermittent connectivity) and if we have to rework a particular device, adjacent devices of this sa
Electronics Forum | Mon Dec 13 00:05:28 EST 1999 | Dennis O'Donnell
I can't figure out why everyone is plating everything with gold. According to the J Standard, gold plating should be removed before soldering to the surface. The gold, when left on the surface to be soldered will contaminate the solder joint and ca
Electronics Forum | Mon Feb 27 06:42:37 EST 2006 | Slaine
What are the long term issues with high tin content solders on parts plated with silver over copper? Is it possible that the silver will be absorbed by the solder then over a long period of time the tin will react with the copper causing it to part
Electronics Forum | Mon Dec 06 03:54:57 EST 1999 | Chris May
Hi Russ, I have a similar situation. I have been told that this can be caused by the nickel, over which the gold is plated, can result in suspect joints, embrittlement etc. Some joints can even be weak and broken without much force on some of my boa
Electronics Forum | Wed Feb 03 23:40:26 EST 1999 | Chris G.
| Does anyone know if I will have problems soldering surface mount components to an all hard gold plated PC board. We want to use hard gold similar to gold used for edge fingers because our customer is concerned about wear and conductivity of connect
Electronics Forum | Wed Feb 03 16:45:20 EST 1999 | Mark Henebry
Does anyone know if I will have problems soldering surface mount components to an all hard gold plated PC board. We want to use hard gold similar to gold used for edge fingers because our customer is concerned about wear and conductivity of connector