Electronics Forum | Thu Apr 20 05:57:55 EDT 2006 | Huub
Do you have experience with wear resistance of spring contacts on ENIG vs Flash Au? regards, Huub.
Electronics Forum | Thu Apr 20 13:42:23 EDT 2006 | fredericksr
I've seen embrittlement %s down to 3%, but a standard 5 mil solder pad would require well over 100uIn of plated gold to cause embrittlement. -Other Russ
Electronics Forum | Wed Mar 29 22:10:59 EST 2006 | davef
Kevslatvin When you visit the machine suppliers, why don't you time the setup of your 25 reels of components as part of your assessment?
Electronics Forum | Mon Apr 03 19:57:49 EDT 2006 | ajca20
Take a kit to your prospective pick N place company and whatch or help set it up. So you can see what it takes.
Electronics Forum | Mon Mar 27 22:41:59 EST 2006 | davef
Design to IPC standards unless a supplier provides documentation on why a change to the standard was necessary. Throw all supplier data sheets in the trash.
Electronics Forum | Tue Mar 28 11:27:37 EST 2006 | smartasp
Hi Samir You are spot on. Exept the glossy surface. For us exactly the oposite. Who is Wavemaster Larry? Smartasp
Electronics Forum | Wed Mar 29 05:23:41 EST 2006 | Rob
Larry is an exponent of Newton's third law - the law of reciprocal actions. You've no doubt heard of the font of all knowledge, well Larry is the equal & opposite of this. (There has also been considerable discussion as to whether he has his own su
Electronics Forum | Wed Mar 29 16:29:19 EST 2006 | steve
"After reading that, I have to go bang my head on the wave." Promise us you'll let it cool first, eh?
Electronics Forum | Thu Mar 30 08:43:14 EST 2006 | russ
Does your fluxer provide for very fine atomization of the flux or is it more "droplet like" Great term huh?
Electronics Forum | Tue May 09 14:19:52 EDT 2006 | Larry (not THAT Larry)
Smartasp - What are your lead to hole ratios like? Dial down the flux and open up the holes, if you can. Keeping at least a 14-20 mil gap between min hole/max lead solves the hole fill problem. L