Electronics Forum | Tue May 03 12:28:45 EDT 2005 | jh0n!
I hate to start to drag this off-topic, but I just had someone here interject that perhaps going to 20x20 and using a different adaptor would be the way we should go, due to the cost difference. Can you (or anyone) quickly identify a few reasons why
Electronics Forum | Wed May 18 03:13:28 EDT 2005 | grantp
Hi, We place BGA, but until now have not used X-Ray inspection, and it would be a good thing to have. Can anyone recommend a low cost X-Ray that would get us by. We don't need something fast, but it should be able to show us clearly voids etc. Reg
Electronics Forum | Thu May 19 17:03:11 EDT 2005 | splice1
Hi all, There are no ground layers which makes the non wetting rate a bit confounding. The foam fluxer has not been cleaned in a while though, while there is a strong evidence of fluxing by running blank paper and looking up the top side
Electronics Forum | Tue Jun 14 10:48:03 EDT 2005 | Paul
We evaluated several machines a couple of years ago and ended up selecting an Agilent SJ50. Fast machine but very limited on joint inspection. Also does not detect missing components reliably which you would normally take as a given on an AOI system.
Electronics Forum | Sat May 28 03:05:42 EDT 2005 | ajaydoshi
We also face same problem . It is difficult to make understand pruchase & store department. They order exact qty & issue also exact qty , later stage we have to take as process loss. They always worry about small cost but never calculte production
Electronics Forum | Mon May 30 03:13:49 EDT 2005 | Joris Groot Koerkamp
Hi rob, We use the component for a long time and never had a problem with the reflow process. Since the component is Leadfree we see the problems. We have the same problem with defferent pcb's. The tin not always flows to the same direction. I check
Electronics Forum | Fri Jun 03 05:31:21 EDT 2005 | grantp
Hi, Yes, and I mean to update that old thread. Things are working really well now we have changed over. Looking for a buyer for the MYDATA now, and we are going to unload the vapor phase and manual printer, and some long conveyers. Need to add it al
Electronics Forum | Mon Jul 03 22:48:42 EDT 2006 | eyryren
Dear ve7khz We are the manufacturer of SMT accessorial material.stencil clean roll and splice tape.We are can manufacture many style stencil clean roll for kinds of screen printer machine and splice tape special for kinds of placement machine. If yo
Electronics Forum | Sat May 28 06:43:03 EDT 2005 | steve
I have the ability to offer both SAC and SN100C lead free alloys to my customer base. What might occur if a customer is already using SAC305 in their wave and they want to save money and go to SN100C. They now are mixing, tin,silver,copper with tin,c
Electronics Forum | Wed Jun 01 03:49:30 EDT 2005 | devilhitam
I'am having a problem with 0805 component where right after placement, the component tend to move from the pad. I'am using 'horse shoe' aperture for 0805 component to resolve the solder beading issue. Does this 'horse shoe' contributing the skew/shif