Electronics Forum | Wed Mar 03 18:42:29 EST 2010 | 89jeong
Hello Graham Copper. Thanks for yr comment. I will review the pad size and component placement with our engineer. It looks that the placement of lead is wrong. But what i want to hear from you is about solder lump on the right.As you can see, the sol
Electronics Forum | Wed Mar 03 23:07:59 EST 2010 | davef
If your "engineer reviewed the reflow profile and said this was not related to reflow conditions," then what does he think it's related to? We think that a increased effort to improve the thermal recipe to solder this part is required, because: * S
Electronics Forum | Fri Mar 05 02:59:59 EST 2010 | grahamcooper22
Hi, Do you have a picture on one of these leads where the solder has covered the lead ? As this is a gull wing device I wouldn't expect solder to cover it. I expect to see a toe fillet / wetting around the sides of the lead and a heel fillet. If your
Electronics Forum | Sat Mar 06 17:45:29 EST 2010 | isd_jwendell
Unfortunately, what you are calling a good fillet is not a good fillet. Solder on the top of the IC lead does not help to make a good connection. The most important fillet is the one located at the heel (think of the IC lead where it meets the PCB as
Electronics Forum | Tue Mar 09 14:23:03 EST 2010 | zanolli
Hello SMTnetters We have a unique application requiring cleaning of an aggressive OA flux. A vapor degreasing process or the immersion of the parts in boiling solvents has some process advantages over an ultrasonic aqueous process. These advantages
Electronics Forum | Tue Mar 09 14:53:16 EST 2010 | davef
Resistivity Of Solvent Extract [ROSE] is a bulk ion contamination [BIC] test method. It should thought of as a process control tool used to assess ionic contaminants. Don't consider it an acceptable tool for establishing 'GO-NOGO' limits. The stan
Electronics Forum | Wed Mar 10 18:42:34 EST 2010 | 89jeong
Hello Sir. We also encountered the same pin-hole issue but there was around MLCC.I also looked for some information in technical report and internet, But i failed to get an answer. As you know this pin hole or blow hole is caused by the solder boilin
Electronics Forum | Thu Mar 11 03:03:26 EST 2010 | grahamcooper22
Hi , Looking at your photo....can I also see a hole in the middle of the joint on the chip component ? Maybe its not just a problem with th ejoint son diodes ? Did you also get mid chip solder balls on chips? If so, I'd almost guarantee the pcb has t
Electronics Forum | Wed Mar 10 00:21:34 EST 2010 | geocep
I have recently purchased an ACE Kiss 101A Selective Solder System 4 weeks ago. I am having a terrible experience. The nozzle will not stay wet, and the flux-er pattern continues to shift erratically; all leading to very poor quality process. ACE
Electronics Forum | Wed Mar 10 16:19:34 EST 2010 | swag
We have one and it's awesome. No problems & training and install was great. The only problem we have had in a couple years is inconsistent nozzle fountain (lasted a day or two until we figured it out). It was our fault - an operator had mixed hand