Electronics Forum | Thu Aug 22 05:00:47 EDT 2002 | kbayley
The reply from J. Baldwin details the most frequent causes of Board Transfer issues on the DEK 288 machine. The DEK.com web site offers a variety of Process, Service and Support details on all DEK products, with the ability to contact the DEK Custom
Electronics Forum | Thu Sep 12 10:51:34 EDT 2002 | genny
Thanks, all. Natasha, thanks for your private email - probably the most beneficial of anything I received. I can't seem to get the reply function to work, so I'm posting here. Just a general suggestion (personal feeling) for posting on this forum.
Electronics Forum | Mon Sep 23 12:27:47 EDT 2002 | dragonslayr
Genny - are you still out there? I'm just a bit curious how your progress has been since your original question was posted weeks ago. It appears you have received a wealth of information. It also is evident that your posting has taken on a new tange
Electronics Forum | Fri Sep 13 14:33:32 EDT 2002 | Simon
Thanks to all of you. This is very kind. I'll have a good poke around the circuit board for loose / hot components - good tips. I think it might be a throw away job, but I thought I'd give it a last try. You guys have actually given me much more
Electronics Forum | Mon Sep 23 12:42:15 EDT 2002 | dragonslayr
yea - yippie- Scott's the man!!!! good answer - I support the notion that in the long run, stopping the line, getting the root cause determination, is not only effective but efficient. It is hard to do because we all are so used to fire fighting on
Electronics Forum | Wed Sep 25 09:24:54 EDT 2002 | caldon
Michael- Please when concidering you U-sonic machine, keep in mind possible chemistries Petroferm, Kyzen, Aqueous technologies, and Zestron products. All are good products and all need to be evaluated with your stencils. Depending on your component t
Electronics Forum | Wed Oct 09 20:52:27 EDT 2002 | davef
Russ, Be careful on how you determine your liquidous point. Sure 205-210�C is fine if your paste and the solderability protection on pads and component leads are near eutectic solder and things worked according to plan, but in real life it doesn't
Electronics Forum | Wed Oct 09 08:56:42 EDT 2002 | pjc
If I understand your question: I've done this before by creating a spreadsheet in Excel. All the data you're looking for can be built into said spreadsheet. I don't think you'll find a "canned" package with the values without buying a bigg-ass prgram
Electronics Forum | Mon Oct 14 08:29:37 EDT 2002 | cyber_wolf
I don't think that anyone is saying we want to barr reps at all. I think the issue is that people get irritated when when certain reps work their sales shpeels into a forum response that does not warrant it.That's all. I value this site tremendously
Electronics Forum | Mon Oct 14 18:30:49 EDT 2002 | seand
Hello all, My tankard is hoisted on high. I always feel that it's good to get a good discussion going with alot of input. My thanks go out to all who have and continue to respond. Sometimes the best outcomes come from the most hotly debated topi