Electronics Forum | Tue Mar 11 16:55:24 EDT 2008 | edmneb
I agree that wave soldering is probably your best method. Of course if you can, tin the wires in a solder pot before insertion into the board. The solder that would be there will probably facilitate wetting a bit better. If you absolutely have to
Electronics Forum | Fri Mar 07 04:53:12 EST 2008 | vinitverma
Hi Wayne, First, all Gem machines including Topaz, TopazX, Sapphire, etc... have the same feeders. You can use either FV feeders (which were the ones when Topaz was introduced), or CL feeders (which came when Topaz X was introduced). Both types of f
Electronics Forum | Wed Mar 12 14:49:43 EDT 2008 | hussman
In the past we would have defects from our CyberCentry and we would just make up excuses to keep running. After reflow the areas of concern exceeded IPC standards. I believe it all depends on how well the machine reads the hieght of the paste and h
Electronics Forum | Sat Jun 12 17:51:30 EDT 2010 | userrich
BIRAL LUBRICANTS IN NORTH AMERICA NOW ALL COME FROM WWW.ADVANTAGELUBES.COM THIS IS THE ONLY FACTORY DIRECT SUPER WAREHOUSE FOR BIRAL LUBRICANTS. THIS WAREHOUSE HAS GREATLY EXPANDED INVENTORIES AND MUCH IMPROVED SERVICE PLUS THEY SHIP OUT LIGHTNING F
Electronics Forum | Tue Mar 11 13:12:56 EDT 2008 | swag
Careful when you get them! I ordered some overnight some time ago because I was too disorganized to have spares. An operator set a heavy steel vise base on top of the bag-o-bulbs while I was taking off the camera cover and crushed all the new ones.
Electronics Forum | Thu Mar 13 09:24:56 EDT 2008 | scotceltic
We use a program called Circuitcam by Aegis. It allows you to import all types of Cad and associate the parts to the different processes. Ex. SMT, Radial, Inspection, Hand Insert. (Customizable depending on your process) Once this is complete it
Electronics Forum | Fri Mar 14 05:38:42 EDT 2008 | meritajs
Hello Could somebody inform us about real consumption of lead free solder alloy SN100C on your wave solder process. We do not use some antiaxidant and had had alloy consumption about 1 kg per hour. What is your experiance? All sugestion will be well
Electronics Forum | Mon Mar 24 16:49:42 EDT 2008 | paulv
Fellows, First of all, thank you for taking the time to respond to the post, however some of you missunderstood the main objective of it. I was basically trying to find historical and current average market prices for solder products. Metal informati
Electronics Forum | Tue Mar 25 17:37:59 EDT 2008 | hussman
If the component "fell off" sounds like double sided reflow - which is most likely a profile issue. If the parts just don't solder, could be many variables. I've had supervisors accuse ovens for bad profiles cuase they had missing parts. Too bad
Electronics Forum | Wed Apr 02 15:35:27 EDT 2008 | jdengler
Our AOI machine can save various views of the same part number since we all know that different manufacturers will mark parts differently, some manufacturers vary their own marks. We get parts from the same manufacturer but different date codes that