| | |Hi all | | This Debate on lead free soldering is really hotting up here in Europe. From 2004 the use of lead in components and assemblies will be banned here. Also flame retardent halogens will be banned(FR4 etc). While we all agree that we hav
Electronics Forum | Wed Dec 30 17:34:23 EST 1998 | Michael Allen
I'm afraid we don't agree regarding the best test method to use here. My understanding is as follows. The omegameter test measures board-level, ionic contamination (i.e., average for the entire board area and all components); it does not tell you w
Electronics Forum | Tue Jan 05 10:17:25 EST 1999 | Earl Moon
| | | Does anyone have any experience with vibration testing of BGA packages and assemblies? We are starting to design BGA's into some of our products and we have not found very much information on vibrational test results. Any information will be
Electronics Forum | Tue May 05 15:45:37 EDT 1998 | Dave F
| Looking to buy used or new tubes, that will fit an SOIC-16 | Need these tubes ASAP. We need to bake these parts and drypack. | Please email or call if you can help. | Eric Jenkins | 801 956-0897 Eric I'm not sure of the manufacturer of the parts th
Electronics Forum | Thu Oct 26 08:59:56 EDT 2000 | Antonio A. Medina
Ok guys, I need help. Here's the deal. We're getting micro solder balls under discreets on the bottomside of the board. Here's my set up... MPM screener w/vacuum plate 6 mil metal screen with 90% circular (rounded) apertures 7 mil (measured) past
Electronics Forum | Wed Oct 25 12:24:02 EDT 2000 | Philip
Hi Chris! I hope this will help you! The CBGA uses an array of high melting point solder spheres(Sn10/Pb90) to connect its ceramic chip carrier to an epoxy glass (FR4) PCB using eutectic (Sn63/Pb37) solder joints at both ceramic and card inter
Electronics Forum | Wed Nov 01 12:10:20 EST 2000 | Jeff
charles, i can appreciate the hand held "reel to reel" scanner as a good solution that is very cost effective. during my smt supervision days we had a number of part loading checks. 1. load plan check, 2. scan check, 3. reel to reel manual check.
Electronics Forum | Tue Jul 18 20:10:09 EDT 2000 | Dave F
Hey Bud: Thanks for the response the other day. We currently use "Jeff�s Method #2: The Drummel Tool." Short answer to your brother is ... yes, probably. Expanding a bit: � It would be surprising not to use a flux to help reflow the solder balls
Electronics Forum | Tue Apr 11 20:26:16 EDT 2000 | Dave F
Jeremy: Parts assembler make leads of either Alloy 42 (Invar, whatever) or copper. The solderability of these leads are protected with eutectic or non-eutectic tin/lead solder, palladium or some palladium alloy, or gold. Cuppla things to consider:
Electronics Forum | Mon Jan 22 15:01:32 EST 2001 | aiscorp
CIM systems for electronics assembly have traditionally considered the PCB only. Final assembly "modules" are often attached to traditional systems to accommodate this common requirement for pre-PCB assembly, mechanical assembly, and final assembly