Electronics Forum: immerse tin (Page 1 of 28)

About immersion tin

Electronics Forum | Mon Oct 06 09:55:35 EDT 2003 | davef

While you are waiting for others to reply, search the fine SMTnet Archives on: * immersion and tin * imm and tin

Re: Immersion tin process

Electronics Forum | Thu Dec 21 20:09:01 EST 2000 | Dave F

You are one lucky person to have access to the fine SMTnet Archives. They have over a hundred threads on immersion tin, white tin, and the other variants.

About immersion tin

Electronics Forum | Sun Oct 05 06:37:41 EDT 2003 | christ

Hi all: I want to know the parameter and criterion about the process of immersion tin,could you be kindly to give me the hins about it in more detail.Thank you for your support. Best wishes christ

About immersion tin

Electronics Forum | Wed Oct 08 06:55:36 EDT 2003 | christ

Hi Dave: Thanking in advance for your valuable response!

Immersion tin process

Electronics Forum | Thu Dec 21 15:58:49 EST 2000 | Josue Jacquez

Hi Guys! I'm looking for information regarding the Tin immersion process. Is somebody there with such info? Could you send me or explain me the process? I'll appreciate your help.

Immersion tin process

Electronics Forum | Thu Dec 21 15:57:36 EST 2000 | Josue Jacquez

Hi Guys! I'm looking for information regarding the Tin immersion process. Is somebody there with such info? Could you send me or explain me the process? I'll appreciate your help.

Pcb immersion tin thickness

Electronics Forum | Wed Aug 09 08:06:07 EDT 2006 | davef

See "IPC-4554 Specification for Immersion Tin Plating for Printed Circuit Boards" 3.2.1 Immersion Tin Thickness. The most common reason for solderability issues with the white tin surface coating during multiple thermal excursions is a thin white ti

Pcb immersion tin thickness

Electronics Forum | Mon Aug 07 09:04:09 EDT 2006 | molos21

Hi everyone, I am starting to use the lead free process and I had a few wetting problems (solder did not reach top side) at the wave soldering process once the pcb had passed our smt line (one heat pass). From what I understand, I have had a problem

White tin pcb, smt production

Electronics Forum | Tue Mar 01 10:21:55 EST 2005 | davef

IPC Plating Committee is presently working on a specification for immersion tin [IPC-4554 Specification for Immersion Tin Plating for Printed Circuit Boards] as a solderable surface finish. Immersion tin is normally deposited at 30 to 60 microinches.

White tin immersion finish

Electronics Forum | Wed Jul 29 13:44:45 EDT 1998 | David Spilker

We are investigating alternatives to HASL finishes for more dense PWBs. OSP is not a good choice because of low solid flux and possibly long shelf life. Immersion gold is expensive and so far has been more difficult to wave solder. Has anyone had

  1 2 3 4 5 6 7 8 9 10 Next

immerse tin searches for Companies, Equipment, Machines, Suppliers & Information

Sell Your Used SMT & Test Equipment

Software for SMT placement & AOI - Free Download.
Non-heated dispensing system

Orange Sticks, Wiring Aids & Probes for Soldering & Desoldering.


High Throughput Reflow Oven
vision placer pnp creator

ONLINE IPC Training & Certification