Electronics Forum | Fri Jul 12 22:15:56 EDT 2013 | ericrr
Sorry to build up your hopes. The latest thing to hit the air ways at work, I was accessed of fiddling with the oven settings, because there were reports of "cracked joints" there was no mention of where the cracks were, cracked at the pcb or cracke
Electronics Forum | Fri Jul 26 12:41:25 EDT 2013 | gallionc
We've had similar "disputes" with our quality department. A technical engineer from Nordson told me that the flourescents in the coating can look faint depending on the angle in which you look at the surface as well as how solder joints reflect the
Electronics Forum | Fri Aug 30 22:51:14 EDT 2013 | cvogel
IPC-J-STD-001E in regards to Ionic Cleanliness standards states less than 1.56 µg/cm² of total NaCL. Assuming a typical electronic process which involves smt, wave, and post-hand soldering and uses NO-Clean flux throughout all process, is it typi
Electronics Forum | Fri Sep 06 14:03:18 EDT 2013 | horchak
If you are a CEM you are setting yourself up for failure and will be left holding the bag. Flash gold has one purpose. It is a protective coating for the base medal to keep it from oxidizing. It is very thin and will be absorbed into the solder joint
Electronics Forum | Fri Sep 20 01:39:21 EDT 2013 | winson16
gold, one of the stablest elements on the > periodic table oxidising. Are you sure, and why > would you want to reduce the vision fail rate on > a part that is clearly shockingly poor? Old inventory is holding a huge material cost and if i can f
Electronics Forum | Fri Sep 20 00:22:41 EDT 2013 | jvadillo
Thanks for the comment regarding the CPH. In fact, the benchtop oven we have takes 7 minutes to complete a batch soldering, so you can imagine that our production volume will not be very high. We can parallelize PCB assembly and oven phase. But defi
Electronics Forum | Sun Sep 29 13:04:58 EDT 2013 | KIC-Tech Service
Sr. Tech, As far as I’m aware, most if not all, manufactures of thermal profilers offer K type thermocouples as a standard for profiling in the electronics manufacturing industry. In my decades of experience in the reflow and wave solder industry, t
Electronics Forum | Fri Sep 27 15:37:05 EDT 2013 | tuxlab
We are thinking of getting a small pcb assembly setup for a small manufacturing co-op here in Los Angeles. Our experience consist of manual soldering of through hole and smt components. A quick search suggests that there are a few turn key opt
Electronics Forum | Thu Oct 17 21:13:35 EDT 2013 | hegemon
But where does it go, that it needs to be refreshed or replenished on the stencil? Does that "just like wax" product wind up in my solder joints, no matter how small the percentage, and would it then qualify as a contaminant? I heard there are some (
Electronics Forum | Sun Nov 10 15:36:06 EST 2013 | davef
Assuming your conformal coating material was selected with the intent of living a life in contact with oil, why doesn't your coating meet the IPC-A-610D requirement of that there be no voiding, no breaks in the surface, no loss of adhesion, etc? Furt