Effects of Packaging Materials on the Lifetime of LED Modules Under High Temperature Test
Published: |
November 18, 2014 |
Author: |
Lei Nie, Wenjing Xiang - Hubei University of Technology, Mingxiang Chen, Huajing Li, Quan Chen - Huazhong University of Science and Technology |
Abstract: |
Performance degradation of packaging material is an important reason for the lifetime reduction of LED. In order to understanding the failure behavior of packaging material, silicone and phosphor were chosen to fabricate LED samples within which an aging test at 125℃ was performed. The result of online luminance measurement showed that LED samples with both silicone and phosphor had the highest luminance decay rate among all test samples because the carbonization of silicone and the consequent outgassing reduced the luminance quickly. The result of the luminance variance with test time was analyzed and an exponential decay model was developed with which the lifetime of LED under high temperature could be estimated.... |
|
Company Information:
More SMT / PCB assembly technical articles »
- Aug 20, 2024 - Thermal Interface Materials Drive Electronic Innovation | GPD Global
- Aug 20, 2024 - Underfill Materials Dispensing in Electronics Manufacturing Applications | GPD Global
- Jul 15, 2024 - Transforming LED Manufacturing: I.C.T Engineers Set Up Complete Production Line in Tajikistan | I.C.T ( Dongguan ICT Technology Co., Ltd. )
- Jun 20, 2024 - Case study: Precise Coating on Electronic Hearing Devices | ASYMTEK Products | Nordson Electronics Solutions
- Mar 19, 2024 - What is Underfill | GPD Global
- Browse Technical Library »
Effects of Packaging Materials on the Lifetime of LED Modules Under High Temperature Test article has been viewed 850 times