Effect of Thermal Aging on Solderabilityof ENEPIG Surface Finish Used in Printed Circuit Boards
Published: |
December 29, 2021 |
Author: |
MaanBajnaid, Emily Holtzhouser, Jordan Terrell, Lawrence Yeh |
Abstract: |
Medtronic seeks to quantify the thermal aging limits of electroless Ni-electroless Pd-immersion Au (ENEPIG) surface finishes to determine how aggressive the silicon burn-in process can be without loss of solderability. Silicon burn-in (power testing at elevated temperature) is used to eliminate early field failures, critical for device reliability. Thermal aging due to burn-in or annealing causes Ni and Pd diffusion to and oxidation on the surface. Surface oxides limit wetting of the PbSn solder, affecting electrical connectivity of components soldered afterburn-in. Isothermal aging of two ENEPIG surface finishes was performed at 75°C-150°C for 100 hrs-1500hrs to test the thermal aging limits and identify how loss of solderability occurs.... |
|
|
|
|
|
|
You must be a Company Information:
More SMT / PCB assembly technical articles »
- Jul 15, 2024 - Transforming LED Manufacturing: I.C.T Engineers Set Up Complete Production Line in Tajikistan | I.C.T ( Dongguan ICT Technology Co., Ltd. )
- Jun 20, 2024 - Case study: Precise Coating on Electronic Hearing Devices | ASYMTEK Products | Nordson Electronics Solutions
- Mar 19, 2024 - What is Underfill | GPD Global
- Mar 19, 2024 - Made in Japan: Solder Paste Jet Dispensing Machine | I.C.T ( Dongguan ICT Technology Co., Ltd. )
- Feb 26, 2024 - Precision Control in Electronic Assembly: Selective Wave Soldering Machine | I.C.T ( Dongguan ICT Technology Co., Ltd. )
- Browse Technical Library »
Effect of Thermal Aging on Solderabilityof ENEPIG Surface Finish Used in Printed Circuit Boards article has been viewed 279 times